Polycarbonate
SABIC Innovative Plastics
產(chǎn)品說明：
LEXAN 945A Polycarbonate (PC) resin is a non-filled, injectionmoldable grade. This non-chlorinated, non-brominated flameretardant PC has an UL-94 V0 rating and is available in transparentand tinted color options. LEXAN 945A is a general purpose resindesigned to meet the needs of various applications.
物性信息：
| 基本信息 |
|
|---|
| | |
| 添加劑 | |
| 特性 | |
| 用途 | |
| 外觀 | |
| 加工方法 | |
| 多點數(shù)據(jù) | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Flexural DMA (ASTM D4065) Pressure-Volume-Temperature (PVT - Zoller Method) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Creep (ASTM D2990) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)
|
| 物理性能 | 額定值 | 單位制 | 測試方法 |
|---|
| 比重 | 1.19 | g/cm3 | ASTM D792 |
| 熔流率（熔體流動速率） (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238 |
| 收縮率 - 流動 (3.20 mm) | 0.60 到 0.80 | % | 內(nèi)部方法 |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
|---|
| 拉伸模量 1 | 2270 | MPa | ASTM D638 |
| 抗張強度 2 |
|
| ASTM D638 |
| 屈服 | 62.0 | MPa | ASTM D638 |
| 斷裂 | 67.0 | MPa | ASTM D638 |
| 伸長率 3 |
|
| ASTM D638 |
| 屈服 | 6.0 | % | ASTM D638 |
| 斷裂 | 130 | % | ASTM D638 |
| 彎曲模量 4(50.0mm 跨距) | 2370 | MPa | ASTM D790 |
| 彎曲強度 5(屈服,50.0 mm 跨距) | 101 | MPa | ASTM D790 |
| 沖擊性能 | 額定值 | 單位制 | 測試方法 |
|---|
| 懸壁梁缺口沖擊強度 (23°C) | 800 | J/m | ASTM D256 |
| 裝有測量儀表的落鏢沖擊 (23°C, TotalEnergy) | 79.0 | J | ASTM D3763 |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
|---|
| 載荷下熱變形溫度 |
|
| ASTM D648 |
| 0.45 MPa, 未退火, 3.20mm | 137 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 3.20mm | 126 | °C | ASTM D648 |
| 維卡軟化溫度 | 143 | °C | ASTM D1525 6 |
| 線形熱膨脹系數(shù) |
|
| ASTM E831 |
| 流動 : -40 到40°C | 6.8E-5 | cm/cm/°C | ASTM E831 |
| 橫向 : -40 到40°C | 7.4E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 120 | °C | UL 746 |
| RTI | 130 | °C | UL 746 |
| 電氣性能 | 額定值 | 單位制 | 測試方法 |
|---|
| 耐電弧性 7 | PLC 7 |
| ASTM D495 |
| 相比耐漏電起痕指數(shù)(CTI) | PLC 2 |
| UL 746 |
| 高電弧燃燒指數(shù)(HAI) | PLC 3 |
| UL 746 |
| 高電壓電弧起痕速率 (HVTR) | PLC 3 |
| UL 746 |
| 熱絲引燃 (HWI) | PLC 2 |
| UL 746 |
| 可燃性 | 額定值 | 單位制 | 測試方法 |
|---|
| UL 阻燃等級 |
|
| UL 94 |
| 0.800 mm | V-2 |
| UL 94 |
| 3.04 mm | V-0 |
| UL 94 |
| 灼熱絲易燃指數(shù) (1.00 mm) | 960 | °C | IEC 60695-2-12 |
| 熱燈絲點火溫度 (1.00 mm) | 850 | °C | IEC 60695-2-13 |
| 極限氧指數(shù) | 35 | % | ISO 4589-2 |
| 注射 | 額定值 | 單位制 |
|
|---|
| 干燥溫度 | 120 | °C |
|
| 干燥時間 | 2.0 到 4.0 | hr |
|
| 建議的Zui大水分含量 | 0.020 | % |
|
| 料斗溫度 | 60.0 到 80.0 | °C |
|
| 料筒后部溫度 | 260 到 280 | °C |
|
| 料筒中部溫度 | 270 到 290 | °C |
|
| 料筒前部溫度 | 280 到 310 | °C |
|
| 射嘴溫度 | 270 到 290 | °C |
|
| 加工（熔體）溫度 | 280 到 310 | °C |
|
| 模具溫度 | 80.0 到 110 | °C |
|